Process for single and multiple level metal-insulator-metal integration with a single mask

ABSTRACT

Method of fabricating a MIM capacitor and MIM capacitor. The method includes providing a substrate including a dielectric layer formed on a first conductive layer and a second conductive layer formed over the dielectric layer, and patterning a mask on the second conductive layer. Exposed portions of the second conductive layer are removed to form an upper plate of a MIM capacitor having edges substantially aligned with respective edges of the mask. The upper plate is undercut so that edges of the upper plate are located under the mask. Exposed portions of the dielectric layer and the first conductive layer are removed using the mask to form a capacitor dielectric layer and a lower plate of the MIM capacitor having edges substantially aligned with respective edges of the mask.

FIELD OF THE INVENTION

The present invention relates to a single and multiple level metal-insulator-metal (MIM) integration.

BACKGROUND DESCRIPTION

According to the known art, MIM integration utilizes a separate mask to define each MIM plate, i.e., two (2) masks for a single MIM and three (3) masks for a dual MIM in all Cu BEOL Integration. For the aluminum MIM version, the bottom plate is formed of the same material as the wiring level so that an extra mask is needed only for the top plate in single MIM or for the top and middle plates in dual MIM.

For higher capacitance, more mask levels are required, which makes the MIM more expensive. After HiK, super high capacitance MIMs will only be possible with more MIM levels. Thus, there is a need for cheaper integration in order to increase MIM levels without adding further masking levels.

A conventional process for dual MIM integration is shown in FIGS. 1-5. A capacitor 100 to be formed is shown having a conductive top plate 101, e.g., titanium nitride (TiN), a first dielectric layer 102, e.g., silicon dioxide (SiO₂), SiN, Hi-K materials, a conductive second plate 103, e.g., TiN, a second dielectric layer 104, e.g., SiO₂, SiN, Hi-K materials, and a conductive bottom plate 105. Bottom plate 105, which may be a sandwiched conductor of more than one metal, e.g., titanium nitride/tungsten/titanium nitride (TiN/W/TiN), is formed on an insulating layer 106, e.g., SiO₂, acting as an etch stop layer, which is formed on insulating layer 107, e.g., silicon nitride, acting as a diffusion barrier from conductors 108, e.g., copper.

In a second step, depicted in FIG. 2, in the formation of capacitor 100, a resist 110, formed of a resist material suitable for the etching to be performed, is placed over top plate 101. Portions of plate 101 lying outside of mask 101 are removed, e.g., via etching, to first dielectric layer 102. In a third step in the process, shown in FIG. 3, a second mask 120, is placed over upper layer 101, i.e., to envelop the entire layer, and onto first dielectric layer 102 to define the geometry of second plate 103. The portions of first dielectric layer 102 and second plate 103 outside of mask 120 are removed to second dielectric layer 104. In a fourth step in the process, shown in FIG. 4, a third mask 130 is placed over upper layer 101, first dielectric layer 102, and second layer 103, i.e., to envelop the entireties of these layers, and onto second dielectric layer 104 to define the geometry of bottom plate 105. The portions of second dielectric layer 104 and bottom plate 105 outside of mask 130 are removed to etch stop layer 106. In the fifth step shown in FIG. 5, the dual MIM parallel wiring is coupled from conductor 112 to capacitor 100 through vias 114, 115, 116, and 117, e.g., copper, and from conductor 113 to capacitor 100 through via 118, e.g., copper.

SUMMARY OF THE INVENTION

The present invention is directed to a method of fabricating a MIM capacitor. The method includes providing a substrate including a dielectric layer formed on a first conductive layer and a second conductive layer formed over the dielectric layer, and patterning a mask on the second conductive layer. Exposed portions of the second conductive layer are removed to form an upper plate of a MIM capacitor having edges substantially aligned with respective edges of the mask. The upper plate is undercut so that edges of the upper plate are located under the mask. Exposed portions of the dielectric layer and the first conductive layer are removed using the mask to form a capacitor dielectric layer and a lower plate of the MIM capacitor having edges substantially aligned with respective edges of the mask.

The invention is directed to a method of fabricating an MIM capacitor from a substrate having a first conductive layer and a second conductive layer separated by a first dielectric layer. The method includes placing a mask on the first conductive layer, removing exposed portions of the first conductive layer outside of the mask, such that a periphery of the first conductive layer essentially aligns with a periphery of the mask, and pulling back the periphery of the first conductive layer, such that the periphery of the first conductive layer is located under the mask. The method further includes removing exposed portions of the first dielectric layer and the second conductive layer outside of the mask, such that a periphery of the first dielectric layer and the second conductive layer essentially align with the periphery of the mask.

The invention is directed to a MIM capacitor having a plurality of conductive layers having peripheries that increase from a top plate to a bottom plate, and a plurality of dielectric layers having a same periphery that corresponds to the periphery of said bottom plate.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-5 illustrate a conventional dual MIM integration;

FIGS. 6-11 illustrate a single MIM integration in accordance with the features of the present invention;

FIG. 12 illustrates the pull back of the exposed layer below its dielectric;

FIG. 13 illustrates the linear relationship between pull back and exposure time;

FIGS. 14-24 illustrate a multiple level MIM integration in accordance with the features of the present invention;

FIG. 25 illustrates an embodiment in which a resist layer is stripped prior to wet etching;

FIG. 26 illustrates an embodiment in which wet etching is performed prior to stripping a resist layer; and

FIG. 27 illustrates an embodiment in which a resist layer is stripped from a dielectric layer prior to wet etching the layer below the dielectric layer.

DETAILED DESCRIPTION OF EMBODIMENTS OF THE PRESENT INVENTION

The invention relates to a method of forming a metal-insulator-metal (MIM) capacitor using a single masking step. In accordance with the invention, layers of upper metal/dielectric/lower metal are formed over a substrate, and a masking layer is formed over the upper metal and the layers are patterned. Portions of the upper metal are removed (i.e., by wet or dry etch) selective to the dielectric to form the upper capacitor plate. According to the invention, an integration scheme allows multiple MIM level integration with a single mask. In particular, integration of the MIM is achieved through a combination of hardmask and plasma etches.

In contrast to conventional processes, which utilized a number of masks even for single MIM integration, the present invention utilizes only a single mask even for multiple MIM integration. An exemplary embodiment of the instant invention directed to single MIM integration is shown in FIGS. 6-11. The process begins with the formation of the substrate through blanket film deposition, as shown in FIG. 6. In particular, a hard mask 200, which may be a single insulator or a sandwiched insulator composed of more than one element, e.g., SiO₂/SiN is positioned over a conductive top layer 101, e.g., TiN, TaN, tungsten, aluminum, or any other suitable conductor, which is provided over bottom conductive layer 105, which may be a single conductor or a sandwiched conductor formed of more than one metal, e.g., TiN/W/TiN, Ta/TaN, or any suitable conductor, and first dielectric layer 102, e.g., SiO₂, SiN, Hi-K materials, aluminum oxide, tantalum oxide, hafnium oxide, zirconium oxide, or other suitable dielectric. As in the conventional processes, bottom plate 105 is formed on an insulating layer 106, e.g., SiO₂ or any suitable insulator, acting as an etch stop layer, which is formed on insulating layer 107, e.g., silicon nitride or other suitable insulator, acting as a diffusion barrier with conductors 108, e.g., copper or other suitable conductor.

A resist 201 is placed on hardmask 200, as shown in FIG. 7. Resist 201 is configured to define the dimensions of bottom plate 105 for the completed MIM capacitor 100′. Portions of hardmask 200, as well as portions of top layer 201 outside of resist 201/hardmask 200 are removed, e.g., via etching, e.g., reactive ion etching (RIE), down to first dielectric layer 102, as shown in FIG. 8. Resist layer 201 is then removed, e.g., via conventional plasma stripping. As shown in FIG. 9, portions of first layer 101 below hardmask 200 are pulled back via plasma etching, e.g., CF4 plasma pull back. Moreover, the pull back can be in a range of 300-800 nm, and preferably 500 nm. FIGS. 12 and 13 are provided to show, by way of example, the use of CF4 plasma when the conductor is TiN. Of course, when other conductors are utilized instead of TiN, other more suitable plasmas may be utilized without departing from the spirit of the invention. Moreover, suitable plasmas for specific conductors can be determined by analyzing the relevant chemistries. FIG. 12 shows a scanning electron microscope image of CF4 plasma pull back of 40 s in TiN, in which the layer beneath the dielectric is pulled back 150 nm. It is noted that plasma pressure and power can be varied to reduce etch time. FIG. 13 graphically illustrates the linear relationship of CF4 etch time versus TiN pull back length. As shown in FIG. 13, the x-axis represents CF4 etch time(s) and the y-axis represents TiN pull back length in nm. At 20 s etch time, the pull back length is about 76 nm, at 30 s etch time, the pull back is about 112 nm, and at 40 s etch time, the pull back length is about 150 nm. Thus, the TiN pull back length over time is a linear function defined by the equation y=3.8x−1.3333.

The process for forming capacitor 100′ continues in FIG. 10 in which bottom 105 is etched to match the dimensions of hardmask 200 down to etch stop layer 106. Subsequently, as illustrated in FIG. 11, the single MIM parallel wiring is coupled from capacitor 100 to conductors through vias, e.g., copper. It is noted that hardmask 200 is not removed from the device, since, as the device will be embedded in SiO₂, the hardmask will become part of the embedding oxide. It is further noted that the dimensions of the top electrode determines device characteristics.

Thus, the present invention can be used to form a single layer MIM capacitor while utilizing only a single mask.

Moreover, an advantage of the instant invention is that the number of MIM levels is independent of the number of mask levels. That is, dimensions of a bottom plate can be defined by a mask, e.g., a hardmask, exposing the portions of the first plate to be pulled back. As all plates will be pulled back during plasma etching, it is preferred to expose only the plate to be pulled back. Further, as some of the hardmask will be etched at every level, the hardmask thickness should be sufficient to survive the number of levels to be etched, where n (i.e., 1, 2, 3, 4 . . . ) is the number of MIM levels to be integrated. A series of plasma etches (pullback) and metal reactive ion etching (RIE) is used to complete the MIM integration.

In another exemplary embodiment of the instant invention, multiple level MIM integration is shown in FIGS. 14-24. The process for forming capacitor 300 begins with the formation of the chip through blanket film deposition, as shown in FIG. 14. As shown in FIG. 14, the chip includes four conductive layers 301, 303, 305, and 307, e.g., TiN, TaN, tungsten, aluminum, or any other suitable conductor, above conductive bottom plate 309, which may be a single conductor or a sandwiched conductor formed of more than one metal, e.g., TiN/W/TiN, Ta/TaN, or any suitable conductor, in which each layer is separated by a dielectric layer 302, 304, 306, and 308 e.g., SiO₂, SiN, Hi-K materials, aluminum oxide, tantalum oxide, hafnium oxide, zirconium oxide, or other suitable dielectric. A hard mask 310, which may be a single insulator or a sandwiched insulator composed of more than one element e.g., SiO₂/SiN or other suitable insulator, is positioned over top layer 301. Further, bottom plate 309 can be formed on an insulating layer 312, e.g., SiO₂ or other suitable insulator, acting as an etch stop layer, which is formed on insulating layer 313, e.g., silicon nitride or other suitable insulator acting as diffusion barrier, that is connected to conductors 314, e.g., copper or other suitable conductor.

A resist 311 is placed on hardmask 310 that is positioned over conductive top layer 301, as shown in FIG. 15, to define hardmask 310 and the dimensions of bottom plate 309 for the completed MIM capacitor 300. Once in place, portions of hardmask 310 and conductor 301 outside of resist 311 are removed, e.g., via etching, such as RIE, down to first dielectric layer 302. Moreover, after defining hardmask 310, resist 311 can be removed by any conventional process, such as plasma stripping. As shown in FIG. 16, portions of first layer 301 below hardmask 310 are pulled back via plasma etching, e.g., CF4 plasma pull back, as discussed above.

As shown in FIG. 17, a second etching is performed in which portions of dielectric 302 and second plate 303 outside of hardmask 310 are removed down to second dielectric layer 304. As all conductor plates will be pulled back during plasma etching, conductor plates are exposed one at a time. In this regard, as shown in FIG. 18, portions of first layer 301 and second layer 303 below their respective dielectric layers 310 and 302 are pulled back via CF4 pull back. In this regard, it is noted that both exposed layers 301 and 303 are pulled back according to the linear relationship discussed above. Moreover, as hardmask 310 will be degraded during each successive etching procedure, hardmask 310 should be selected to have a thickness sufficient to complete the number of levels to be etched, e.g., greater than 1000 Å.

In FIG. 19, a third etching is performed in which portions of dielectric 304 and third plate 305 outside of hardmask 310 are removed down to dielectric layer 306. Next, portions of first layer 301, second layer 303, and third layer 305 below their respective dielectric layers 310, 302, and 304 are pulled back, as shown in FIG. 20.

A fourth etching is shown in FIG. 21, in which exposed portions of dielectric 306 and fourth plate 307 outside of hardmask 310 are removed down to dielectric layer 4. Again, portions of first layer 301, second layer 303, third layer 305, as well as fourth layer 307, below their respective dielectric layers 310, 302, 304, and 306 are pulled back, as shown in FIG. 22.

In FIG. 23, exposed portions of dielectric 308 and bottom plate 309 are removed down to etch stop layer, such that the dimensions of bottom plate 309 correspond to the dimensions of mask 310. Thus, the instant invention provides a multiple layer MIM integration while requiring only a single mask. Subsequently, as illustrated in FIG. 24, the multiple level MIM parallel wiring is coupled from capacitor 300 to conductors, e.g., copper, through vias, e.g., copper.

While the above exemplary embodiments have been described with a hardmask, it is noted that, in accordance with the present invention, the masking layer can be a soft mask (i.e., photoresist) or a hard mask (i.e., silicon nitride) without departing from the scope and spirit of the invention.

In particular, while the above exemplary embodiments have been directed to plasma etching, it may be advantageous to utilize wet etching, as discussed below.

According to another feature of the invention, the resist layer can be removed, e.g., via plasma stripping, prior to the step of removing, i.e., pulling back, portions of the upper metal layer. In this embodiment, illustrated in FIG. 25, a resist layer 400 can be placed on conductive top layer 401, e.g., platinum or other suitable conductor for wet etching, separated from conductive bottom plate 403, which can be a single conductor or a sandwiched conductor composed of more than one metal, e.g., TiN/W/TiN, Ta/TaN, by a dielectric layer 402, e.g., Ta₂O₅. Resist layer 400 defines the dimensions of bottom plate 403, such that exposed portions of the top and bottom layers are removed in a single etching procedure. Next, a resist strip removes resist layer 400, and a subsequent wet etch process, which will effect only the platinum layer, pulls back portions of top layer 401. However, because the top surface of the top conductor 401 is exposed to the wet etch, a certain degradation in thickness occurs.

In a further exemplary embodiment, the resist can remain during the step of pulling back portions of the upper metal layer. In this regard, FIG. 26 illustrates a resist layer 500 placed on top layer 501, e.g., platinum, separated from bottom plate 503, e.g., TiN/W/TiN, by a dielectric layer 502, e.g., Ta₂O₅. Resist layer 500 defines the dimensions of bottom plate 503, such that exposed portions of the top and bottom layers are removed. Next, a wet etch process pulls back portions of top layer 501 only, and then a resist strip removes resist layer 500. In contrast to the process shown in FIG. 25, because the resist protects the top surface of top conductor 501, the wet etching does not degrade the thickness of conductive layer.

A further exemplary process for performing the RIE and pull back is illustrated in FIG. 27. In particular, a resist layer 600 can be placed on a dielectric layer 601 covering top layer 602, e.g., platinum. Top layer 602 can be separated from bottom plate 604, e.g., TiN/W/TiN, by a dielectric layer 603, e.g., Ta₂O₅. Resist layer 600 defines the dimensions of bottom plate 604, such that exposed portions of the top and bottom layers are removed at the same time. Next, a resist strip removes resist layer 400 from dielectric layer 401, and a subsequent wet etch process pulls back portions of top layer 602 below dielectric layer 601. In this embodiment, the dielectric layer acts to protect the upper surface of top conductor 602 so that the wet etching does not adversely affect the thickness of the conductor.

Advantageously, the instant invention provides an almost unlimited number of MIM levels without adding mask costs, and enables super high capacitance capabilities, which is required when the limit of HiK is reached. In this regard, the present invention produces an MIM with less reliability degradation for multiple levels to increase capacitance density than thinning down the film, as in conventional processes.

While the invention has been described in terms of exemplary embodiments, those skilled in the art will recognize that the invention can be practiced with modifications and in the spirit and scope of the appended claims. 

1. A MIM capacitor formed by the following process: providing a substrate including a dielectric layer formed on a first conductive layer and a second conductive layer formed over said dielectric layer; positioning a hard mask over said second conductive layer; positioning a resist over the hard mask as a mask pattern; removing exposed portions of said hard mask and said second conductive layer to form an upper plate of a MIM capacitor having edges substantially aligned with respective edges of said mask; undercutting said second conductive layer so that edges of said second conductive layer are located under said hard mask; and removing exposed portions of said dielectric layer and said first conductive layer using said hard mask to form a capacitor dielectric layer and a lower plate of said MIM capacitor having edges substantially aligned with respective edges of said hard mask, wherein the MIM capacitor comprises: the hard mask is disposed over and above an entire top surface of said second conductive layer of the formed MIM capacitor to form at least a part of an embedding oxide; said first conductive layer, said dielectric layer and said hard mask have a same width dimension; said second conductive layer has a width dimension that is smaller than the respective widths of said first conductive layer, said dielectric layer and said hard mask; said second conductive layer is sandwiched between and in direct contact with said dielectric layer and said hard mask such that a top surface of said second conductive layer is entirely covered by said hard mask; said hard mask entirely covers the top surface of said second conductive layer and extends past edges thereof; and the hard mask has an upper and a lower surface, and the entire upper and lower surfaces are planar.
 2. The MIM capacitor of claim 1, wherein sidewalls of said dielectric layer, said first conductive layer, and said second conductive layers are devoid of contact with said hard mask.
 3. A MIM capacitor including a substrate having a first conductive layer and a second conductive layer separated by a first dielectric layer, said MIM capacitor being formed by the following process: placing a hard mask and resist over the first conductive layer, removing exposed portions of the hard mask and first conductive layer outside of the resist, such that a periphery of the first conductive layer essentially aligns with a periphery of the resist, pulling back the periphery of the first conductive layer, such that the periphery of the first conductive layer is located under the hard mask, removing exposed portions of the first dielectric layer and the second conductive layer outside of the hard mask, such that a periphery of the first dielectric layer and the second conductive layer essentially align with the periphery of the hard mask, and forming at least another conductive layer separated from the second conductive layer by a dielectric layer, wherein the MIM capacitor comprises: a plurality of at least three conductive layers have an increasing periphery from a top plate to a bottom plate, each of said at least three conductive layers being separated by a dielectric layer and each of the dielectric layers having a same width dimension; the hard mask remaining over the top plate of the formed MIM capacitor which corresponds in a width dimension to that of each of the dielectric layers; and at least one via for coupling the formed MIM capacitor to a conductor, the at least one via being arranged one of to or through the hard mask of the formed MIM capacitor.
 4. The MIM capacitor in accordance with claim 3, wherein the hard mask is structured and arranged to become at least part of an embedding oxide.
 5. The capacitor of claim 3, wherein the dielectric layer directly contacting a top surface of the bottom plate has a same width dimension as the bottom plate.
 6. The MIM capacitor of claim 3, wherein sidewalls of said plurality of dielectric layers, and said plurality of conductive layers are devoid of contact with said hard mask.
 7. A MIM capacitor comprising: a plurality of conductive layers having peripheries that increase from a top plate to a bottom plate; a plurality of dielectric layers arranged between the top and bottom plates, separated by at least one of the plurality of conductive layers, having a same periphery that corresponds to the periphery of said bottom plate; a hard mask structured and arranged as at least a part of an embedding oxide being non-removably connected to and over an entire top surface of the top plate, wherein edges of the top plate are located below the hard mask; and a first interconnect via and a second interconnect via passing through the hard mask, wherein: said hard mask has a same width dimension as said plurality of dielectric layers and said bottom plate; said hard mask is comprised of a upper surface and a lower surface, said upper surface and lower surface of the hard mask being planar surfaces; the lower surface of said hard mask contacts the entire top surface of said top plate such that the top surface of said top plate is in contact only with the lower surface of said hard mask and the lower surface of said top plate only makes direct contact with a surface of a lower dielectric layer of said plurality of dielectric layers; said first interconnect via passes through the hard mask and contacts the second conductive layer; and said second interconnect via passes through the hard mask and contacts the first conductive layer bypassing the second conductive layer such that said second interconnect via is disposed in a region between the edges of said top plate and the edges of the hard mask.
 8. The MIM capacitor of claim 7, wherein an upper surface of the top plate is planar and is in direct contact with only said hard mask.
 9. The MIM capacitor of claim 8, wherein an entirety of a bottom surface of said top plate contacts said dielectric layer between said top plate and said bottom plate.
 10. The MIM capacitor of claim 9, wherein said hard mask extends entirely along a top surface of said top plate and past edges thereof without contacting sides of said top plate.
 11. The MIM capacitor of claim 10, wherein said top plate makes contact on its upper and lower surfaces only with said hard mask and said dielectric layer, respectively.
 12. The MIM capacitor of claim 7, wherein sidewalls of said plurality of dielectric layers, and said plurality of conductive layers are devoid of contact with said hard mask.
 13. A MIM capacitor comprising: a substrate; a first conductive layer on said substrate; a dielectric layer on said first conductive layer; a second conductive layer over said dielectric layer; and a hard mask over and above an entire upper surface of said second conductive layer, said hard mask directly covering an entire upper surface of said second conductive layer and said hard mask being incorporated into said MIM capacitor as at least a part of an embedding oxide, wherein: edges of said dielectric layer are substantially aligned with respective edges of said hard mask and edges of said first conductive layer such that said first conductive layer, said dielectric layer and said hard mask have substantially equal width dimensions; said second conductive layer has a width dimension that is smaller than said first conductive layer, said dielectric layer and said hard mask; said second conductive layer is in direct contact with said dielectric layer; and the hard mask has an upper and a lower surface, and the entire upper and lower surfaces are planar.
 14. The MIM capacitor in accordance with claim 13, further comprising: a plurality of interconnect vias structured and arranged to connect said formed MIM capacitor to a conductor, wherein said vias include: one or more first interconnect vias passing through said hard mask and contacting said second conductive layer, and one or more second interconnect vias passing through said hard mask, contacting said first conductive layer, and bypassing said second conductive layer such that said second interconnect vias are disposed in a region between said edges of said conductive layer and said edges of said hard mask.
 15. The MIM capacitor of claim 14, wherein: the second conductive layer is comprised of an upper surface and a lower surface, said upper surface and said lower surface of said second conductive layer being planar surfaces, the dielectric layer is comprised of an upper surface and a lower surface, said upper surface and said lower surface of said dielectric layer being planar surfaces; the lower surface of said hard mask is in direct contact with said entirety of said upper surface of said second conductive layer and entirely covers said upper surface of said second conductive layer; and the upper surface of said dielectric layer is in direct contact with said entirety of said lower surface of said second conductive layer and entirely covers said lower surface of said second conductive layer.
 16. The MIM capacitor of claim 15, wherein said lower surface of said hard mask extends past said edges of said second conductive layer without contacting sides of said second conductive layer.
 17. The MIM capacitor of claim 16, wherein: said upper surface of said second conductive layer only contacts said lower surface of said hard mask and said one or more first vias; and said lower surface of said second conductive layer only contacts said upper surface of said dielectric layer and without directly contacting said plurality of interconnect vias.
 18. The MIM capacitor of claim 13, wherein said edges of said hard mask extend beyond said edges of said second conductive layer.
 19. The MIM capacitor of claim 18, wherein sidewalls of said dielectric layer, said first conductive layer, and said second conductive layer are devoid of contact with said hard mask.
 20. A MIM capacitor comprising: a plurality of at least three conductive layers separated by a plurality of dielectric layers; and a hard mask over a top conductive layer of said plurality of conductive layers, said hard mask being incorporated into said MIM capacitor as at least a part of an embedding oxide covering said top conductive layer, wherein: said plurality of conductive layers have an increasing periphery from said top conductive layer to a bottom conductive layer of said plurality of conductive layers, a periphery of said top conductive layer is located within a periphery of said hard mask, a periphery of said bottom conductive layer is substantially aligned with a periphery of said hard mask, and peripheries of said plurality of dielectric layers are substantially aligned with said periphery of said hard mask.
 21. The MIM capacitor in accordance with claim 20, wherein said edges of said hard mask extend beyond said peripheries of said plurality of conductive layers except for said periphery of said bottom conductive layer.
 22. The MIM capacitor in accordance with claim 21, further comprising: a plurality of interconnect vias structured and arranged to connect said formed MIM capacitor to a conductor, said vias including: one or more first interconnect vias passing through said hard mask and contacting said top conductive layer without contacting others of said plurality of conductive layers, one or more second interconnect vias passing through said hard mask and contacting said bottom conductive layer bypassing others of said plurality of conductive layers, and one or more third interconnect vias passing through said hard mask, contacting a third of said plurality of conductive layers and bypassing others of said plurality of conductive layers.
 23. The MIM capacitor of claim 22, wherein: said hard mask is comprised of an upper surface and a lower surface, said upper surface and lower surface of said hard mask being planar surfaces; said top conductive layer is comprised of an upper surface and a lower surface, said upper surface and lower surface of said top conductive layer being planar surfaces, said top dielectric layer is comprised of an upper surface and a lower surface, said upper surface and lower surface of said top dielectric layer being planar surfaces; said lower surface of said hard mask is in direct contact with an entirety of said upper surface of said second conductive layer and entirely covers said upper surface of said second conductive layer; and said upper surface of said dielectric layer is in direct contact with an entirety of said lower surface of said second conductive layer and entirely covers said lower surface of said second conductive layer.
 24. Said MIM capacitor of claim 23, wherein said lower surface of said hard mask extends past edges of said upper surface of said top conductive layer without contacting sides of said top conductive layer.
 25. Said MIM capacitor of claim 23, wherein: said upper surface of said top conductive layer only contacts said lower surface of said hard mask and said one or more first interconnect vias; and said lower surface of said top conductive layer only contacts said upper surface of said top dielectric layer and does not contact said plurality of interconnect vias.
 26. Said MIM capacitor of claim 23, wherein edges of said hard mask extend beyond edges of said second conductive layer.
 27. Said MIM capacitor of claim 26, wherein sidewalls of said dielectric layers, said first conductive layer and said second conductive layer are devoid of contact with said hard mask. 